Simriz Compound
|
Elastomer
|
Hardness (Shore A)
|
Application
|
Color
|
Temp
(°C) |
|
FFKM
|
90
|
Simriz134 is a high strength, high Durometer Perfluoroelastomer developed for CPI and HPI applications. |
Black
|
300
|
|
|
FFKM
|
70
|
General purpose, Excellent Chemical Compatibility, acids, Steam/hot water, Chemical & Hydrocarbon processing, aromatic/aliphatic Oils, ethers |
Black
|
230
|
|
|
FFKM
|
75
|
USP Class VI, FDA compliant, wide chemical resistance, excellent heat resistance |
Black
|
230
|
|
|
FFKM
|
75
|
General purpose, Excellent Chemical Compatibility, acids, Steam/hot water, Chemical & Hydrocarbon processing, aromatic/aliphatic Oils, ethers |
Black
|
230
|
|
|
FFKM
|
75
|
General purpose, Excellent Plasma resistance, low particulation, Deposition, Plasma Etch, Metalization, Ion Implant |
White
|
230
|
|
|
FFKM
|
75
|
High temperature, Wet processes, Etching, stripping, Copper plating |
Black
|
300
|
|
|
FFKM
|
70
|
High temperature, Excellent Plasma resistance, low particulation, Deposition, Plasma Etch, Metalization, Ion Implant, RTP, oxidation, diffusion, lamp anneal |
White
|
300
|
|
|
FFKM
|
65
|
High purity, Excellent Plasma resistance, low particulation & Extraction, Deposition, Plasma Etch, Metalization, Ion Implant, RTP, oxidation, diffusion |
Clear
|
280
|
|
|
FFKM
|
80
|
General purpose, improved chemical and solvent resistance including Nitric acid and amine chemicals |
Black
|
230
|
|
|
Enhanced FKM
|
75
|
General purpose, plasma resistance, Deposition, Plasma Etch, Metalization, Ion Implant, lithography |
Black
|
220
|
|
|
Enhanced FKM
|
85
|
General purpose, plasma resistance, Deposition, Plasma Etch, Metalization, Ion Implant, lithography |
Off-White
|
200
|
|
|
Enhanced FKM
|
75
|
High Performance, plasma resistance, minimal particulation, Deposition, Plasma Etch, Metalization, Ion Implant, CVD, lithography |
Ivory
|
150
|
 |
 |
 |
 |
 |
||||
 |
 |
 |
 |
 |
||||
 |
 |
 |
 |
 |
||||
 |
 |
 |
 |
 |
||||
 |
 |
 |
 |
 |
||||
 |
 |
|
|||||